➤ Quinate calibrated tech (5 times) for smooth finish

➤ Anti-Fungal and Anti-Bacterial coating

➤ Fire-Resistant with lower smoke generation and low flammability

➤ Rate of Burning - >40 minutes

➤ Resists ignition, surface spread, and penetration

➤ Formaldehyde Emission level: E0 as per European stranded

➤ Borer & termite proof

➤ Imported high-density timber

➤ Chemically treated Composed Core & Veneers

➤ Long Calibrated core for a smooth finish

➤ Glue – Hydroxybenzene base adhesive

➤ Structural and engineering application

➤ Hydroxybenzene base adhesive

➤ Hygroscopicity - >13%

➤ 8-10% Moisture content

➤ Density : above 0.70 gm/cm3

➤ Tensile Strength : >480 Kgf/cm2 (in face grain)

➤ Screw-holding strength - >300 Kgf

➤ Nail holding strength - >120 Kgf

➤ Static bending strength MOE:
->7800 N/mm2 (along the face grain)

->4600 N/mm2 (across the face grain)

➤ Wet bending strength: MOE:
Above 4800N/mm2 (Along the face grain)
Above 3600 N/mm2 (Across the face grain)

➤ Face 0.5mm+

➤ Thickness tolerance: up to 4 mm ± 10% above 4 mm ± 5%

➤ Mycological test: complies with the requirement

➤ Glue shear strength (Dry state):1660 N

➤ Glue shear strength (Wet state): 1400 N

➤ Preservative: Acid copper chrome composition

➤ Adhesion of plies: Excellent

➤ Sum of Value: Above 960 kgf/cm2

➤ MOR: Above 60N/mm2 (Along the face grain)
Above 48 N/mm2 (Across the face grain)

➤ Retention of preservation: Above 12Kg/m3

➤ Conforms to IS : 1659

➤ 100% American or other imported Pinewood

➤ Fillers – American Pinewood

➤ Quinate calibrated tech (5 times) for smooth finish

➤ Anti fungal and anti bacteria coating

➤ Formaldehyde Emission level: E1 as per European standard

➤ Borer, fungus & termite proof.

➤ 100% American or other imported pine wood

➤ Chemically treated and seasoned

➤ High dimensional stability strength

➤ Calibrated core for a smooth finish

➤ Face – Gurjan or equivalent

➤ Core – Gurjan / UC/ or equivalent high-density imported Hardwood

➤ Density 0.65 gm/cm3

➤ Moisture content 8 to 15%

➤ Adhesion of plies – excellent

➤ Modulus of elasticity – above 6000 n/mm2

➤ Modulus of rupture – above 60 n/mm2

➤ Preservative – C.C.B Fixed type

➤ Water absorption – below 1%

➤ Screw holding strength – 1100 N

➤ Nail holding strength – 600 N

➤ Thickness: ±5%

➤ Preservative Treatment: B/B.A. treatment in battens